Fabrication of zirconia- and ceria-based thin-wall tubes by thermoplastic extrusion

TRUNEC, M.

Originální název

Fabrication of zirconia- and ceria-based thin-wall tubes by thermoplastic extrusion

Typ

článek v časopise - ostatní, Jost

Jazyk

angličtina

Originální abstrakt

Thin-wall tubes made of zirconia stabilized by 8 mol% of yttria and of ceria doped by 10 mol% of gadolinia were prepared by thermoplastic extrusion. The rheological behaviour of the ceramic mixtures prepared and the effect of rheological properties on the deformation of tubes were studied. After sintering, the diameter of tubes was 10.5 mm and their wall thickness ranged from 270 to 420 mm. The deformation and shape irregularity of sintered tubes were determined. The tubes, which were sintered at a temperature of 1500 degC, had a relative density of more than 98% t.d. Flexural strength and fracture toughness of sintered ceramics were determined on test bars prepared by injection moulding from thermoplastic mixtures identical to those used for extrusion. The fracture toughness established was 1.7 MPa m0.5 for yttria-stabilized zirconia, and 1.1 MPa m0.5 for gadolinia-doped ceria.

Klíčová slova

extrusion, suspensions, ZrO2, CeO2, electrolyte

Autoři

TRUNEC, M.

Rok RIV

2004

Vydáno

1. 1. 2004

Nakladatel

Elsevier Science

ISSN

0955-2219

Periodikum

Journal of the European Ceramic Society

Ročník

24

Číslo

4

Stát

Spojené království Velké Británie a Severního Irska

Strany od

645

Strany do

651

Strany počet

7

URL

knihovna VUT v Brně, FSI

BibTex

@article{BUT41949,
  author="Martin {Trunec}",
  title="Fabrication of zirconia- and ceria-based thin-wall tubes by thermoplastic extrusion",
  journal="Journal of the European Ceramic Society",
  year="2004",
  volume="24",
  number="4",
  pages="7",
  issn="0955-2219",
  url="knihovna VUT v Brně, FSI"
}