Fracture of Irradiated Austenitic Stainless Steel with Special Reference to Irradiation Assisted Stress Corrosion Cracking

HOJNÁ, A. MICHALICKA, J. SRBA, O.

Original Title

Fracture of Irradiated Austenitic Stainless Steel with Special Reference to Irradiation Assisted Stress Corrosion Cracking

English Title

Fracture of Irradiated Austenitic Stainless Steel with Special Reference to Irradiation Assisted Stress Corrosion Cracking

Type

journal article - other

Language

Czech

Original Abstract

This paper deals with fracture of neutron irradiated austenitic Ti-stabilized stainless steel 08Ch18N10T. The steel had been tested in air and in water environment (320C) using several tests representing different stress strain conditions for crack initiation and growth; Slow Strain Rate and Crack Growth Rate tests were performed in the water. Without irradiation the steel did not suffer from stress corrosion cracking in the water, but on irradiated specimens appeared areas of intergranular fracture mixed with transgranular cleavage-like facets and secondary cracks typical for IASCC phenomenon. The differences between fracture of irradiated and non-irradiated specimens in air and in water are documented and discussed.

English abstract

This paper deals with fracture of neutron irradiated austenitic Ti-stabilized stainless steel 08Ch18N10T. The steel had been tested in air and in water environment (320C) using several tests representing different stress strain conditions for crack initiation and growth; Slow Strain Rate and Crack Growth Rate tests were performed in the water. Without irradiation the steel did not suffer from stress corrosion cracking in the water, but on irradiated specimens appeared areas of intergranular fracture mixed with transgranular cleavage-like facets and secondary cracks typical for IASCC phenomenon. The differences between fracture of irradiated and non-irradiated specimens in air and in water are documented and discussed.

Keywords

Irradiation Assisted Stress Corrosion Cracking, austenitic stainless steel, neutron irradiation, ductile fracture, intergranular fracture

Key words in English

Irradiation Assisted Stress Corrosion Cracking, austenitic stainless steel, neutron irradiation, ductile fracture, intergranular fracture

Authors

HOJNÁ, A.; MICHALICKA, J.; SRBA, O.

RIV year

2014

Released

1. 1. 2014

ISBN

1662-9795

Periodical

Key Engineering Materials (web)

Year of study

2013

Number

592 - 593

State

Swiss Confederation

Pages from

569

Pages to

572

Pages count

4

BibTex

@article{BUT102663,
  author="Anna {Hojná} and Jan {Michalička} and Ondřej {Srba}",
  title="Fracture of Irradiated Austenitic Stainless Steel with Special Reference to Irradiation Assisted Stress Corrosion Cracking",
  journal="Key Engineering Materials (web)",
  year="2014",
  volume="2013",
  number="592 - 593",
  pages="569--572",
  issn="1662-9795"
}