Fatigue Fracture of Turbine Blades: Case Studies

KIANICOVÁ, M. POKLUDA, J.

Original Title

Fatigue Fracture of Turbine Blades: Case Studies

Type

journal article in Web of Science

Language

English

Original Abstract

Fracture surfaces of two sets of rotor blades failed after strong testing procedures of aircraft engines in the test-stand are investigated by means of SEM. While the process of fatigue fracture in the first set of blades did not reveal any defect features, both the initiation and propagation of fatigue cracks was strongly influenced by casting defects

Keywords

Turbine blades; failure analysis; fatigue fracture; casting defects

Authors

KIANICOVÁ, M.; POKLUDA, J.

RIV year

2014

Released

31. 1. 2014

Publisher

Trans Tech Publications

Location

Bern

ISBN

1013-9826

Periodical

Key Engineering Materials (print)

Year of study

592-593

Number

1

State

Swiss Confederation

Pages from

712

Pages to

715

Pages count

4

BibTex

@article{BUT110139,
  author="Marta {Kianicová} and Jaroslav {Pokluda}",
  title="Fatigue Fracture of Turbine Blades: Case Studies",
  journal="Key Engineering Materials (print)",
  year="2014",
  volume="592-593",
  number="1",
  pages="712--715",
  doi="10.4028/www.scientific.net/KEM.592-593.712",
  issn="1013-9826"
}