Detailed Determination of Mechanical Fracture Parameters of Concrete after Fire Experiments

conference paper

English

Detailed Determination of Mechanical Fracture Parameters of Concrete after Fire ExperimentsThe aim of this paper is to describe the procedure of determining the mechanical fracture parameters of selected concrete specimens taken from panels after the fire experiments. The records (in form load vs displacement diagrams) of three-point bending fracture tests of these specimens with initial stress concentrators was first advanced corrected and subsequently evaluated using the Effective Crack Model and the work-of-fracture method. The increasing temperatures during the fire experiments ranging between 550 to 1000 °C led to a decrease of modulus of elasticity and fracture toughness values and to the increase of fracture energy value. The 2D laser profile scanner was used to estimate the degree of complexity of fracture surfaces; its statistical dependence on the mechanical fracture parameters proved to be moderate – the absolute value of the correlation coefficient was about 0.5 [–].

Concrete, high temperature, fracture test, 2D laser profile scanner.

ŠIMONOVÁ, H.; TRČKA, T.; BEJČEK, M.; ROZSYPALOVÁ, I.; DANĚK, P.; KERŠNER, Z.

28. 2. 2018

Trans Tech Publications

Switzerland

978-3-0357-1284-1

Solid State Phenomena: 24th Concrete Days

1012-0394

Solid State Phenomena

272

Swiss Confederation

220

225

6