Cascaded Arc Deposited Diamond Like Hydrogenated Carbon Films

ZAHARIA, T. ZLÁMAL, B.

Original Title

Cascaded Arc Deposited Diamond Like Hydrogenated Carbon Films

Type

conference paper

Language

English

Original Abstract

Diamond like hydrogenated carbon films have been formed on different substrates at very low energies and temperatures by PECVD process employing acetylene as the precursor gas. The plasma source was of a cascaded arc type with Ar as carrier gas. The films grown at ultra fast rates were found a practical thickness limit of ~1 ?m above which delamination from the substrate occurred. Deposition on Si (100), glass and plastic substrates has been studied and the films characterized in terms of sp3 content, roughness, hardness and adhesion. Deposition rates up to 20 nm/sec have been achieved at substrate temperatures below 100C. The typical sp3 content of 60-75% in the films was determined by a combination of XPS and XAES techniques. The hardness and adhesion of the films was measured using a MicroMaterials Nano Test Indenter/Scratch tester. Hardness was found to vary from 5 to 11 GPa depending on the admixed acetylene flow. Adhesion was found to increase drastically when in situ cleaning of the substrate was employed. Modelling of the film growth on Si substrate and of dissociation patterns in the plasma was attempted using HyperChem software.

Keywords

DLC, PECVD, deposition, modelling

Authors

ZAHARIA, T.; ZLÁMAL, B.

RIV year

2005

Released

20. 9. 2005

Publisher

ČSNMT Praha 2005

Location

Brno University of Technology

ISBN

80-214-2984-4

Book

Juniormat '05

Edition

5

Edition number

5

Pages from

199

Pages to

202

Pages count

4

BibTex

@inproceedings{BUT18011,
  author="Theodor {Zaharia} and Bronislav {Zlámal}",
  title="Cascaded Arc Deposited Diamond Like Hydrogenated Carbon Films",
  booktitle="Juniormat '05",
  year="2005",
  series="5",
  number="5",
  pages="199--202",
  publisher="ČSNMT Praha 2005",
  address="Brno University of Technology",
  isbn="80-214-2984-4"
}