Very High Cycle Fatigue Behavior of Austenitic Stainless Steel in Annealed and Predeformed Condition

SARKAR, A. KLUSÁK, J. KOZÁKOVÁ, K. CHRIST, H.-J.

Original Title

Very High Cycle Fatigue Behavior of Austenitic Stainless Steel in Annealed and Predeformed Condition

Type

journal article in Web of Science

Language

English

Original Abstract

Engineering components in service nowadays are designed for a large number of loading cycles (similar to 109), which makes fatigue behavior in this cycle range (designated as very high cycle fatigue [VHCF]) a topic of significant interest. The present study aims to investigate the high cycle fatigue (HCF) and VHCF behavior in type 304 stainless steel in two different conditions (annealed and with a martensite volume fraction of similar to 45 %) through low cycle fatigue predeformation at a subzero temperature. A fatigue diagram in the form of an S-N curve extending up to the VHCF range is generated, which shows different HCF and VHCF behaviors for the annealed and predeformed conditions. Further tests are carried out at different R ratios to generate constant-life Haigh diagrams for both conditions. Although no failure is observed in the VHCF range under the annealed condition, an internal crack initiation mode is observed under the predeformed condition (Type II behavior), which is attributed to the enhanced notch sensitivity under VHCF cycling induced by a significant extent of strain-induced martensite formed during predeformation. To address the influence of varying load history under service, specimens were prefatigued in HCF, followed by VHCF cycling. The HCF-VHCF boundary is found to be significantly impacted by the prior HCF damage, with lowering of the fatigue limit under VHCF.

Keywords

high cycle fatigue; very high cycle fatigue; S-N curve; metastability; austenitic stainless steel

Authors

SARKAR, A.; KLUSÁK, J.; KOZÁKOVÁ, K.; CHRIST, H.-J.

Released

9. 2. 2023

Publisher

AMER SOC TESTING MATERIALS

Location

W CONSHOHOCKEN

ISBN

2379-1365

Periodical

Materials Performance and Characterization

Year of study

12

Number

2

State

United States of America

Pages from

78

Pages to

92

Pages count

15

URL

BibTex

@article{BUT187322,
  author="SARKAR, A. and KLUSÁK, J. and KOZÁKOVÁ, K. and CHRIST, H.-J.",
  title="Very High Cycle Fatigue Behavior of Austenitic Stainless Steel in Annealed and Predeformed Condition",
  journal="Materials Performance and Characterization",
  year="2023",
  volume="12",
  number="2",
  pages="78--92",
  doi="10.1520/MPC20220076",
  issn="2379-1365",
  url="https://www.astm.org/mpc20220076.html"
}