Microstructural Stability of Dissimilar Weld Joint of Creep-Resistant Steels with Increased Nitrogen Content at 500-900stC

ZLÁMAL, B. FORET, R. BURŠÍK, J. SVOBODA, M.

Original Title

Microstructural Stability of Dissimilar Weld Joint of Creep-Resistant Steels with Increased Nitrogen Content at 500-900stC

Type

journal article - other

Language

English

Original Abstract

The structural changes taking place in the dissimilar laboratory welds of 6CrMoV 8-3-2 (T25), being under development, and modified X12CrMoVNb 10-1 (P91) nitrided steels annealed at temperatures of 500-900stC have been subject of study. Carbon and nitrogen redistribution measurement by the EPMA method was complemented with detailed structural analysis aimed at the phase profiles and chemical composition of coexisting carbides and carbonitrides in particular regions of the weld joint. Results of experimental work were compared with thermodynamic and kinetic modelling using the DICTRA software. A very good agreement between the modelling and the experiments was observed.

Keywords

modelling, structural stability, precipitates, weld joint

Authors

ZLÁMAL, B.; FORET, R.; BURŠÍK, J.; SVOBODA, M.

RIV year

2007

Released

1. 3. 2007

Publisher

Trans Tech Publications

ISBN

1012-0386

Periodical

Defect and Diffusion Forum

Year of study

263

Number

3

State

Swiss Confederation

Pages from

195

Pages to

200

Pages count

6

BibTex

@article{BUT44027,
  author="Bronislav {Zlámal} and Rudolf {Foret} and Jiří {Buršík} and Milan {Svoboda}",
  title="Microstructural Stability of Dissimilar Weld Joint of Creep-Resistant Steels with Increased Nitrogen Content at 500-900stC",
  journal="Defect and Diffusion Forum",
  year="2007",
  volume="263",
  number="3",
  pages="195--200",
  issn="1012-0386"
}