Service life prediction for refractory materials

BOCCACCINI, D. CANNIO, M. VOLKOV-HUSOVIC, T. KAMSEU, E. ROMAGNOLI, M. VERONESI, P. LEONELLI, C. DLOUHÝ, I. BOCCACCINI, A.

Original Title

Service life prediction for refractory materials

Type

journal article - other

Language

English

Original Abstract

Ultrasonic pulse velocity testing and image analysis were used to predict the thermal stability of cordierite-mullite refractories. Two compositions used as substrates in fast firing of porcelain whiteware, characterized by different microstructure and crack propagation behavior, were investigated. Fracture strength and fracture toughness values were obtained from three point bending test and chevron notched specimen technique, respectively. The measurement of the ultrasonic velocity was used to assess the material degradation with increasing number of thermal-shock cycles and specimen damage was monitored using image analysis to obtain further evidence of material degradation. The correlation between thermo-mechanical properties, ultrasonic velocity, microstructure, crack-propagation behavior and thermal-shock resistance was discussed. A remarkable similarity was found between the variation of ultrasonic velocity (when measured through the length of the refractory plates) and fracture strength with number of thermal shock cycles. Service life prediction models for refractory plates, from measured values of ultrasonic velocity and surface damage analysis, were proposed and validated.

Keywords

Refractory materials, cordierite-mullite, fracture toughness, ultrasonic pulse velocity, image analysis, service life

Authors

BOCCACCINI, D.; CANNIO, M.; VOLKOV-HUSOVIC, T.; KAMSEU, E.; ROMAGNOLI, M.; VERONESI, P.; LEONELLI, C.; DLOUHÝ, I.; BOCCACCINI, A.

RIV year

2008

Released

3. 4. 2008

Publisher

Springer

Location

USA

ISBN

0022-2461

Periodical

Journal of Materials Science

Year of study

43

Number

12

State

United States of America

Pages from

4079

Pages to

4090

Pages count

12

BibTex

@article{BUT48758,
  author="Dino {Boccaccini} and Maria {Cannio} and Tatjana {Volkov-Husovic} and Elie {Kamseu} and Marcello {Romagnoli} and Paolo {Veronesi} and Cristina {Leonelli} and Ivo {Dlouhý} and Aldo {Boccaccini}",
  title="Service life prediction for refractory materials",
  journal="Journal of Materials Science",
  year="2008",
  volume="43",
  number="12",
  pages="4079--4090",
  issn="0022-2461"
}