Publication detail

The Microstructure Changes in IN713LC during the Creep Exposure

POSPÍŠILOVÁ, S. KIANICOVÁ, M. VLASÁK, T. HUTAŘ, P. PODRÁBSKÝ, T. HAKL, J.

Original Title

The Microstructure Changes in IN713LC during the Creep Exposure

Type

journal article - other

Language

English

Original Abstract

Nickel-based creep resisting alloys (strengthened by Ni3Al,Ti) are the basic materials for high-temperature constructional parts in aircraft engines and energy units. These parts are exposed to combined effects of mechanical stresses, high temperature and dioxide-corrosion conditions. The microstructure changes of cast polycrystalline Ni-based superalloy IN713LC after creep exposure were studied. Three specimens with three different diameters were used for creep tests. The degradation stage (damage parameter ?) was determined for all parts of specimens. Individual parts of specimens were metallographic observed and analyzed by image analysis after rupture. The results were compared with model of stress distribution in the specimen with potential damage in the centre of the specimen.

Keywords

creep, damage parameter, microstructure changes, rafting, image analysis

Authors

POSPÍŠILOVÁ, S.; KIANICOVÁ, M.; VLASÁK, T.; HUTAŘ, P.; PODRÁBSKÝ, T.; HAKL, J.

RIV year

2011

Released

1. 1. 2011

Publisher

TransTech Publication

Location

Switzerland

ISBN

1022-6680

Periodical

Advanced Materials Research

Year of study

278

Number

1

State

Swiss Confederation

Pages from

120

Pages to

125

Pages count

6

BibTex

@article{BUT49976,
  author="Simona {Hutařová} and Marta {Kianicová} and Tomáš {Vlasák} and Pavel {Hutař} and Tomáš {Podrábský} and Jan {Hakl}",
  title="The Microstructure Changes in IN713LC during the Creep Exposure",
  journal="Advanced Materials Research",
  year="2011",
  volume="278",
  number="1",
  pages="120--125",
  issn="1022-6680"
}