Originální název
Bending Fatigue Behaviour of Diffusion and Thermal Barrier Coating Systems
Typ
článek ve sborníku ve WoS nebo Scopus
Jazyk
angličtina
Originální abstrakt
The work is focused on the study of degradation of ZrO2 stabilized by Y2O3 (YSZ) Room temperature fatigue behaviour of two variants of diffusion aluminide coatings and conventional air plasma sprayed CoNiCrAlY + ZrO2-Y2O3 thermal barrier system, which were deposited on a cast nickel-based supperalloy substrate, was studied under symmetrical bending loading regime. The study elucidates the differences in a fatigue crack initiation micromechanism with respect to applied stress level and its impact on the fatigue performance of studied coating systems.
Klíčová slova
Diffusion Coatings; Thermal Barrier Coatings; Fatigue Crack Initiation; Fatigue Life
Autoři
SLÁMEČKA, K.; NĚMEC, K.; ČELKO, L.; HORNÍKOVÁ, J.; POKLUDA, J.; ŠVEJCAR, J.
Rok RIV
2014
Vydáno
1. 4. 2014
Nakladatel
Trans Tech Publications Ltd
Místo
Zurich-Durnten, Switzerland
ISBN
9783037859346
Kniha
Key Engineering Materials
ISSN
1013-9826
Periodikum
Key Engineering Materials (print)
Ročník
592-593
Číslo
1
Stát
Švýcarská konfederace
Strany od
716
Strany do
719
Strany počet
4
URL
http://www.scientific.net/KEM.592-593.716
BibTex
@inproceedings{BUT105551, author="Karel {Slámečka} and Karel {Němec} and Ladislav {Čelko} and Jana {Horníková} and Jaroslav {Pokluda} and Jiří {Švejcar}", title="Bending Fatigue Behaviour of Diffusion and Thermal Barrier Coating Systems", booktitle="Key Engineering Materials", year="2014", journal="Key Engineering Materials (print)", volume="592-593", number="1", pages="716--719", publisher="Trans Tech Publications Ltd", address="Zurich-Durnten, Switzerland", doi="10.4028/www.scientific.net/KEM.592-593.716", isbn="9783037859346", issn="1013-9826", url="http://www.scientific.net/KEM.592-593.716" }