Sintering behavior of feldspar rocks

SOKOLÁŘ, R. VODOVÁ, L.

Originální název

Sintering behavior of feldspar rocks

Typ

článek v časopise - ostatní, Jost

Jazyk

angličtina

Originální abstrakt

Sintering behaviour as dependence of water absorption, flexural strength and firing shrinkage of dry pressed test samples made from three different types of feldspar rocks on the firing temperature (1120 – 1300 °C) was determined. Potassium, potassium-sodium and sodium-calcium industrially milled feldspars with similar granulometry according to equivalent mean spherical diameter of the grains d(0.5) in the range of 16.6 – 20.8 microns were used. The sintering process was described according to changes in mineralogical composition of the fired test samples too. During the sintering process, feldspars gradually disappear in phases – first of all alkali feldspars (albite, microcline); anorthite (calcium feldspar) is more resistant to melting thanks to its higher melting temperature and it increases the sintering temperature of feldspar. Sodium-potassium feldspar Z43NaK50 with the lowest content of alkalis (3.35 % of K2O and 2.67 % of Na2O) and the highest equivalent 2mean spherical diameter d(0.5) showed the most intensive sintering activity.

Klíčová slova

feldspars, sintering, porosity, mineralogical composition

Autoři

SOKOLÁŘ, R.; VODOVÁ, L.

Rok RIV

2014

Vydáno

8. 10. 2014

Nakladatel

IJES

Místo

Gazipur, Bangladesh

ISSN

2319-6483

Periodikum

Research Inventy

Ročník

4

Číslo

10

Stát

Bangladéšská lidová republika

Strany od

49

Strany do

55

Strany počet

7

BibTex

@article{BUT111741,
  author="Radomír {Sokolář} and Lucie {Keršnerová}",
  title="Sintering behavior of feldspar rocks",
  journal="Research Inventy",
  year="2014",
  volume="4",
  number="10",
  pages="49--55",
  issn="2319-6483"
}