Fracture-Mechanics Behaviour of Ceramic Foam with Macroscopic Stress Concentrator upon the Tensile Test

ŠEVEČEK, O. MAJER, Z. BERTOLLA, L. CHLUP, Z. KOTOUL, M.

Originální název

Fracture-Mechanics Behaviour of Ceramic Foam with Macroscopic Stress Concentrator upon the Tensile Test

Typ

článek ve sborníku ve WoS nebo Scopus

Jazyk

angličtina

Originální abstrakt

The work investigates an influence of the macroscopic stress concentrator inside the ceramic open cell foam structure on the fracture-mechanics response of the foam upon the tensile test. As the concentrator, the central crack/rectangular notch was taken into account. The influence of the crack/notch length and width on the stress concentration ahead the concentrator tip was assessed using the simplified FE beam element based model with irregular cells simulating the real ceramic foam structure. Average principal stresses calculated on set of struts ahead the crack/notch tip were compared with average stresses in the intact structure. It was found that the ratio of these stresses increases linearly with the crack length. The stress concentration ratio is slightly lower in case of thick rectangular notch than in case of a thin crack. Furthermore, the failure load leading to complete fracture of the studied specimens, subjected to the tensile loading, were calculated using the same model. It is shown that the difference factor between the critical fracture force in case of structure without concentrator and with concentrator is very close to the concentration factor calculated from the average stresses on particular struts in the region in front of the concentrator tip.

Klíčová slova

Ceramic foam, fracture, stress concentrator, FEM, Voronoi tessellation, tensile test.

Autoři

ŠEVEČEK, O.; MAJER, Z.; BERTOLLA, L.; CHLUP, Z.; KOTOUL, M.

Vydáno

5. 9. 2017

Nakladatel

Trans Tech Publications

Místo

Švýcarsko

ISBN

978-3-0357-1168-4

Kniha

Advances in Fracture and Damage Mechanics XVI

Číslo edice

1

ISSN

1662-9795

Periodikum

Key Engineering Materials (web)

Ročník

754

Číslo

1

Stát

Švýcarská konfederace

Strany od

99

Strany do

102

Strany počet

4

BibTex

@inproceedings{BUT139050,
  author="Oldřich {Ševeček} and Zdeněk {Majer} and Luca {Bertolla} and Zdeněk {Chlup} and Michal {Kotoul}",
  title="Fracture-Mechanics Behaviour of Ceramic Foam with Macroscopic Stress Concentrator upon the Tensile Test",
  booktitle="Advances in Fracture and Damage Mechanics XVI",
  year="2017",
  journal="Key Engineering Materials (web)",
  volume="754",
  number="1",
  pages="99--102",
  publisher="Trans Tech Publications",
  address="Švýcarsko",
  doi="10.4028/www.scientific.net/KEM.754.99",
  isbn="978-3-0357-1168-4",
  issn="1662-9795"
}