TENSILE STRENGTH OF PURE IRON SAMPLES MANUFACTURED BY SELECTIVE LASER MELTING METHOD

ROUPEC, J. MAZŮREK, I. STRECKER, Z. KUBÍK, M. MACHÁČEK, O.

Originální název

TENSILE STRENGTH OF PURE IRON SAMPLES MANUFACTURED BY SELECTIVE LASER MELTING METHOD

Typ

článek ve sborníku ve WoS nebo Scopus

Jazyk

angličtina

Originální abstrakt

This paper deals with the tensile strength measurement of samples produced by additive manufacturing. Tested samples were made of pure iron on machine SLM280HL based on Selective Laser Melting method (SLM). The pure iron was selected as a semi-finished product for future manufacturing of a magnetic circuit in magnetorheological damper. The magnetic circuit is an inseparable part of damper piston, which is high mechanically loaded during the operation. Therefore, it is highly important to have suitable mechanical properties. The free-cutting steel 11SMn30 was used as a reference sample. Five different settings of laser power, scanning speed and hatch distance were used for preparation of five sets of samples. The highest tensile strength was achieved at samples produced with the highest energy per unit area and the lowest volume speed of building. These conditions were achieved by laser power 300 W, scanning speed 750 mm/s and hatch distance 84 m. The tensile strength of these samples was 461 MPa, which is higher than at reference steel (452 MPa). From the point of view of economic aspects, the second most strength steel is better choice, because its tensile strength is 456 MPa but the building is about 50 % faster.

Klíčová slova

Selective Laser Melting, pure iron, tensile strength, magnetorheological valve

Autoři

ROUPEC, J.; MAZŮREK, I.; STRECKER, Z.; KUBÍK, M.; MACHÁČEK, O.

Vydáno

16. 5. 2017

Nakladatel

Institute of Thermomechanics Academy of Sciences of the Czech Republic

Místo

Praha

ISBN

978-80-214-5497-2

Kniha

ENGINEERING MECHANICS 2017

Strany od

830

Strany do

833

Strany počet

4

BibTex

@inproceedings{BUT141680,
  author="Jakub {Roupec} and Ivan {Mazůrek} and Zbyněk {Strecker} and Michal {Kubík} and Ondřej {Macháček}",
  title="TENSILE STRENGTH OF PURE IRON SAMPLES MANUFACTURED BY SELECTIVE LASER MELTING METHOD",
  booktitle="ENGINEERING MECHANICS 2017",
  year="2017",
  pages="830--833",
  publisher="Institute of Thermomechanics Academy of Sciences of the Czech Republic",
  address="Praha",
  isbn="978-80-214-5497-2"
}