Interaction of fatigue and creep in MAR-M 247 superalloy
Typ
článek v časopise ve Scopus, Jsc
Jazyk
angličtina
Originální abstrakt
Lifetime of MAR-M 247 Ni-based superalloy was experimentally studied under high-frequency cyclic loading (120 Hz) with constant tensile mean stress σm = 300 MPa at temperature 900 °C in air. The stress amplitude σa was changed in order to investigate the superalloy lifetime in a wide range of conditions, from pure creep to pure fatigue. The superposition of the stress amplitude on the mean stress does not influence the specimen lifetime until a threshold value is reached. Scanning electron microscopy was utilized for the fracture surface observation with the aim to identify the governing damage mechanisms for particular test conditions.
Klíčová slova
creep/fatigue interaction; superalloy; MAR-M 247; high temperature
Autoři
HORNÍK, V.; FINTOVÁ, S.; ŠMÍD, M.; HUTAŘ, P.; HRBÁČEK, K.; KUNZ, L.
Vydáno
19. 2. 2020
Nakladatel
Elsevier B.V.
ISSN
2452-3216
Periodikum
Procedia Structural Integrity
Ročník
23
Číslo
1
Stát
Italská republika
Strany od
197
Strany do
202
Strany počet
6
URL
https://www.sciencedirect.com/science/article/pii/S2452321620301451
Plný text v Digitální knihovně
http://hdl.handle.net/11012/193515
BibTex
@article{BUT164315, author="Vít {Horník} and Stanislava {Fintová} and Miroslav {Šmíd} and Pavel {Hutař} and Karel {Hrbáček} and Ludvík {Kunz}", title="Interaction of fatigue and creep in MAR-M 247 superalloy", journal="Procedia Structural Integrity", year="2020", volume="23", number="1", pages="197--202", doi="10.1016/j.prostr.2020.01.086", issn="2452-3216", url="https://www.sciencedirect.com/science/article/pii/S2452321620301451" }