Pilot Fracture Tests of Special Fine-Grained Composites

článek ve sborníku ve WoS nebo Scopus

angličtina

Mechanical fracture parameters were obtained for special fine-grained cement-based composites from three-point bending tests. A total of four sets of composite specimens were tested. All of the sets of composites were based on a general recipe and differ in the amount of high-strength aggregate and/or dispersed steel fibres present. Standardized prism specimens with a nominal size of 40 × 40 × 160 mm were used for the fracture tests after 131 days of curing. An initial notch was cut in the centre of the prisms with a depth approximately equal to one third of the specimen’s height. Three specimens from each set of composites were tested in the three-point bending fracture test configuration. Load versus midspan deflection diagrams were recorded. Experimentally obtained load vs displacement diagrams were corrected and analysed using the Effective Crack Model, the Work-of-Fracture method and an independent identification technique using numerical modelling. The most important mechanical fracture parameters, such as static modulus of elasticity, effective fracture toughness, specific fracture energy and effective tensile strength, were determined. Compressive and splitting tensile strength values were obtained from the halves of the specimens left over after the bending tests.

Ultra-high performance composite; fracture test; load–displacement diagram; mechanical fracture parameters; numerical model identification

ROZSYPALOVÁ, I.; BYSTRIANSKA, E.; KOUTNÝ, O.; DANĚK, P.; FRANTÍK, P.; KERŠNER, Z.

9. 8. 2021

Trans Tech Publications Ltd

Switzerland

978-3-0357-3821-6

27th Concrete Days

1662-9779

Solid State Phenomena

322

Švýcarská konfederace

3

8

6