Detail publikace

Characterization of Microstructural Damage and Failure Mechanisms in C45E Structural Steel under Compressive Load

KRAIŠNIK, M. ČEP, R. KOUŘIL, K. BALOŠ, S. ANTIĆ, A. MILUTINOVIĆ, M.

Originální název

Characterization of Microstructural Damage and Failure Mechanisms in C45E Structural Steel under Compressive Load

Typ

článek v časopise ve Web of Science, Jimp

Jazyk

angličtina

Originální abstrakt

In this paper, the microstructural damage evolution of a steel with a ferrite-pearlite microstructure (C45E) was investigated during the process of cold upsetting. The development and the accumulation of microstructural damage were analyzed in different areas of samples that were deformed at different strain levels. The scanning electron microscopy (SEM) results showed that various mechanisms of nucleation of microcavities occurred during the upsetting process. In quantitative terms, microcavities were predominantly generated in pearlite colonies due to the fracture of cementite lamellae. In addition, the mechanism of decohesion had a significant influence on the development of a macroscopic crack, since a high level of microcracks, especially at higher degrees of deformation, was observed at the ferrite/pearlite or ferrite/ferrite interfaces. It was found that the distribution of microcavities along the equatorial plane of the sample was not uniform, as the density of microcavities increased with increasing strain level. The influence of stress state, i.e., stress triaxiality, on the nucleation and distribution of microcracks, was also analyzed.

Klíčová slova

structural steel; microstructure; damage mechanisms; microcracks; upsetting; FEM

Autoři

KRAIŠNIK, M.; ČEP, R.; KOUŘIL, K.; BALOŠ, S.; ANTIĆ, A.; MILUTINOVIĆ, M.

Vydáno

19. 3. 2022

Nakladatel

MDPI

Místo

BASEL

ISSN

2073-4352

Periodikum

Crystals

Ročník

12

Číslo

3

Stát

Švýcarská konfederace

Strany od

1

Strany do

20

Strany počet

20

URL

Plný text v Digitální knihovně

BibTex

@article{BUT177810,
  author="Milija {Kraišnik} and Robert {Čep} and Karel {Kouřil} and Sebastian {Baloš} and Aco {Antić} and Mladomir {Milutinović}",
  title="Characterization of Microstructural Damage and Failure Mechanisms in C45E Structural Steel under Compressive Load",
  journal="Crystals",
  year="2022",
  volume="12",
  number="3",
  pages="1--20",
  doi="10.3390/cryst12030426",
  issn="2073-4352",
  url="https://www.mdpi.com/2073-4352/12/3/426"
}