Analysis of the Causes of Shaft Damage

ZÁBRANSKÝ, K. KLAKURKOVÁ, L. GEJDOŠ, P. JULIŠ, M. ŠVEJCAR, J.

Originální název

Analysis of the Causes of Shaft Damage

Typ

článek ve sborníku ve WoS nebo Scopus

Jazyk

angličtina

Originální abstrakt

The paper deals with complex material analysis of a shaft after failure. The shaft was operated as part of an "Abradable rig" device used to test the resistance of coatings at high speeds, which simulates a turboprop engine's operating conditions. The shaft is made of 16MnCr5 material with subsequent cementation. The subject of interest is a complex material analysis (i.e. control of the chemical composition of the material and complete fractographic and metallographic analysis) and verification of the shaft design. The aim of the study is a precise determination of the specific cause of component failure.

Klíčová slova

shaft failure; cementation; micro-hardness; corrosion; fracture surface; microstructure

Autoři

ZÁBRANSKÝ, K.; KLAKURKOVÁ, L.; GEJDOŠ, P.; JULIŠ, M.; ŠVEJCAR, J.

Vydáno

28. 6. 2022

Nakladatel

Trans Tech Publications Ltd

Místo

Switzerland

ISSN

1662-9795

Periodikum

Key Engineering Materials (web)

Číslo

923

Stát

Švýcarská konfederace

Strany od

133

Strany do

138

Strany počet

6

BibTex

@inproceedings{BUT178739,
  author="Karel {Zábranský} and Lenka {Klakurková} and Pavel {Gejdoš} and Martin {Juliš} and Jiří {Švejcar}",
  title="Analysis of the Causes of Shaft Damage",
  booktitle="Key Engineering Materials",
  year="2022",
  journal="Key Engineering Materials (web)",
  number="923",
  pages="133--138",
  publisher="Trans Tech Publications Ltd",
  address="Switzerland",
  doi="10.4028/p-8nz9sl",
  issn="1662-9795"
}