Anorthite Ceramics: Grog and Clay Selection for Lowering the Sintering Temperature

SOKOLÁŘ, R. NGUYEN, M.

Originální název

Anorthite Ceramics: Grog and Clay Selection for Lowering the Sintering Temperature

Typ

článek v časopise ve Web of Science, Jimp

Jazyk

angličtina

Originální abstrakt

A research investigation was conducted on two variables that are indicative of a plastic raw materials based on kaolin vs. interstratified illite-smectite clay and a non-plastic admixture including grog (quartz vs. alumina) during the sintering process of an anorthite porcelain body beginning at 950 °C, up to the sintering temperature. A correlation was found between the mineralogical composition and various parameters of the fired bodies. A purely anorthic sintered body can be produced using interstratified illite-smectite clay with quartz as a grog, which has the lowest coefficient of linear thermal expansion in the temperature range of 30 to 700 °C and highest bending strength - modulus of rupture of sintered body. When alumina is present in the raw material mixture, the coefficient of linear thermal expansion is lower due to the absence of the SiO2 phases. Quartz in combination with interstratified illite-smectite clay significantly reduces the sintering temperature through the formation of an amorphous melt up to the sintering temperature.

Klíčová slova

anorthite ceramics; mineralogical composition; sintering temperature; coefficient of linear thermal expansion; bending strength

Autoři

SOKOLÁŘ, R.; NGUYEN, M.

Vydáno

21. 2. 2024

Nakladatel

Taylor & Francis Group

Místo

United Kingdom

ISSN

2187-0764

Periodikum

Journal of Asian Ceramic Societies

Ročník

12

Číslo

2

Stát

Japonsko

Strany od

129

Strany do

140

Strany počet

12

URL

Plný text v Digitální knihovně

BibTex

@article{BUT187969,
  author="Radomír {Sokolář} and Martin {Nguyen}",
  title="Anorthite Ceramics: Grog and Clay Selection for Lowering the Sintering Temperature",
  journal="Journal of Asian Ceramic Societies",
  year="2024",
  volume="12",
  number="2",
  pages="129--140",
  doi="10.1080/21870764.2024.2320448",
  issn="2187-0764",
  url="https://www.tandfonline.com/doi/full/10.1080/21870764.2024.2320448"
}