Fatigue Crack Initiation and Propagation in Coated and Uncoated Inconel 713LC at 800 degC

SMÉKALOVÁ, J. POSPÍŠILOVÁ, S. OBRTLÍK, K. JULIŠ, M. PODRÁBSKÝ, T.

Originální název

Fatigue Crack Initiation and Propagation in Coated and Uncoated Inconel 713LC at 800 degC

Typ

článek v časopise - ostatní, Jost

Jazyk

angličtina

Originální abstrakt

Fatigue crack initiation and propagation was studied in cast polycrystalline nickel base superalloy Inconel 713LC in as-received condition and with surface treatment by AlSi protective coating. Cylindrical specimens were cyclically strained under strain control with constant total strain amplitude at 800 ?C. Fatigue fracture surface, specimen surface, and specimen sections were investigated using optical microscopy and scanning electron microscopy. Fatigue crack initiation sites and fatigue crack growth mechanisms were identified and crack propagation rates were obtained base on striation spacing in fracture surfaces. The crack initiation mechanism study revealed reasons for the fatigue life increase in the surface treated material.

Klíčová slova

initiation, fatigue crack propagation, crack propagation rate, fractography, striation

Autoři

SMÉKALOVÁ, J.; POSPÍŠILOVÁ, S.; OBRTLÍK, K.; JULIŠ, M.; PODRÁBSKÝ, T.

Rok RIV

2010

Vydáno

1. 12. 2010

Nakladatel

VŠB Ostrava

Místo

Ostrava

ISSN

1210-0471

Periodikum

Transaction of the VŠB-Technical university of Ostrava, Mechanical series

Ročník

LVI

Číslo

2

Stát

Česká republika

Strany od

155

Strany do

162

Strany počet

8

BibTex

@article{BUT50304,
  author="Jana {Smékalová} and Simona {Hutařová} and Karel {Obrtlík} and Martin {Juliš} and Tomáš {Podrábský}",
  title="Fatigue Crack Initiation and Propagation in Coated and Uncoated Inconel 713LC at 800 degC",
  journal="Transaction of the VŠB-Technical university of Ostrava, Mechanical series",
  year="2010",
  volume="LVI",
  number="2",
  pages="155--162",
  issn="1210-0471"
}