CORROSION FATIGUE OF PROCESS EQUIPMENTS

NEKVASIL, R.

Originální název

CORROSION FATIGUE OF PROCESS EQUIPMENTS

Typ

abstrakt

Jazyk

angličtina

Originální abstrakt

Experience in operation of process equipment all round the world proves that most of the damage on pipes, nozzles, valve pieces and pumps is caused by fatigue. Much of this damage is linked to temperature loading, which leads to multiplication of layers or peel-off of the material; damage is also linked to mechanical loading caused by vibrations. Impact of the loading may be enhanced by corrosion since the material is exposed both to water and high temperatures. Fatigue cracks also appear on outlet pipes of various chemical reactors, at connection of inlet pipes with nozzles and steam devices [1]. These cracks may be explained by corrosion fatigue and stress induced corrosion fractures caused by cyclic loading due to distribution of temperature fields during start up and close-down of operation units.

Klíčová slova

corrosion, fatigue, process equipments

Autoři

NEKVASIL, R.

Vydáno

9. 11. 2009

Nakladatel

Kazimierz Peszyński

Místo

Bydgoszcz

ISBN

978-83-87982-13-3

Kniha

Developments in Machinery Design and Control

Strany od

69

Strany do

70

Strany počet

2

BibTex

@misc{BUT60952,
  author="Richard {Nekvasil}",
  title="CORROSION FATIGUE OF PROCESS EQUIPMENTS",
  booktitle="Developments in Machinery Design and Control",
  year="2009",
  pages="69--70",
  publisher="Kazimierz Peszyński",
  address="Bydgoszcz",
  isbn="978-83-87982-13-3",
  note="abstract"
}