Initiation and Growth of Fatigue Cracks in Inconel 713LC with Al Coating at 800 degC

POSPÍŠILOVÁ, S. OBRTLÍK, K. JULIŠ, M. PODRÁBSKÝ, T.

Originální název

Initiation and Growth of Fatigue Cracks in Inconel 713LC with Al Coating at 800 degC

Typ

článek v časopise - ostatní, Jost

Jazyk

angličtina

Originální abstrakt

This paper is focused on the study of initiation and growth of fatigue cracks in IN713LC with Al protective coating and without coating. Microstructure characteristics and microhardness of Al coating are documented. Fatigue crack initiation and fatigue crack growth mechanisms were identified. The crack propagation rates were obtained based on striation spacing in fracture surfaces.

Klíčová slova

low cycle fatigue, IN713LC, aluminide coating, crack initiation, crack propagation rate

Autoři

POSPÍŠILOVÁ, S.; OBRTLÍK, K.; JULIŠ, M.; PODRÁBSKÝ, T.

Rok RIV

2011

Vydáno

19. 7. 2011

Nakladatel

Chemické listy

Místo

Novotného lávka 5 Praha 1

ISSN

0009-2770

Periodikum

Chemické listy

Ročník

105

Číslo

S

Stát

Česká republika

Strany od

840

Strany do

841

Strany počet

2

BibTex

@article{BUT72857,
  author="Simona {Hutařová} and Karel {Obrtlík} and Martin {Juliš} and Tomáš {Podrábský}",
  title="Initiation and Growth of Fatigue Cracks in Inconel 713LC with Al Coating at 800 degC",
  journal="Chemické listy",
  year="2011",
  volume="105",
  number="S",
  pages="840--841",
  issn="0009-2770"
}