OBRTLÍK, K. POSPÍŠILOVÁ, S. JULIŠ, M. PODRÁBSKÝ, T. POLÁK, J.
Originální název
Effect of Al and AlSi diffusion coating on the low cycle fatigue behavior of Inconel 713LC
Typ
článek v časopise - ostatní, Jost
Jazyk
angličtina
Originální abstrakt
Cylindrical specimens of Inconel 713LC in untreated condition and surface treated with Al and Al-Si diffusion coating were cyclically strained under strain control at 800 deg in air. The structural and hardness characteristics of the hardened surface layer are presented. Cyclic hardening/softening curves, cyclic stress-strain curves, and fatigue life curves are obtained. The sections parallel to the specimen axis have been examined to study fatigue damage mechanisms. The effect of Al coating on stress response and fatigue life slightly differs from that of Al-Si coating.
Klíčová slova
Low cycle fatigue; Inconel 713LC; diffusion coating; cyclic hardening/softening curve; cyclic stress-strain curves; fatigue life curve;
Autoři
OBRTLÍK, K.; POSPÍŠILOVÁ, S.; JULIŠ, M.; PODRÁBSKÝ, T.; POLÁK, J.
Rok RIV
2011
Vydáno
30. 11. 2011
Nakladatel
Elsevier Ltd.
Místo
Nizozemí
ISSN
1877-7058
Periodikum
Procedia Engineering
Ročník
Číslo
10
Stát
Nizozemsko
Strany od
1360
Strany do
1365
Strany počet
6
BibTex
@article{BUT76145, author="Karel {Obrtlík} and Simona {Hutařová} and Martin {Juliš} and Tomáš {Podrábský} and Jaroslav {Polák}", title="Effect of Al and AlSi diffusion coating on the low cycle fatigue behavior of Inconel 713LC", journal="Procedia Engineering", year="2011", volume="2011", number="10", pages="1360--1365", issn="1877-7058" }