Fraktografická rekonstrukce časového průběhu únavového porušování nosníku křídla letounu

AUGUSTIN, P.

Originální název

Fraktografická rekonstrukce časového průběhu únavového porušování nosníku křídla letounu

Anglický název

Fractography reconstruction of time line of fatigue failure of aircraft wing bearer

Typ

článek ve sborníku ve WoS nebo Scopus

Jazyk

čeština

Originální abstrakt

One of the most important parts of the damage-tolerance evaluation of aircraft structure is full-scale fatigue test. This test must demonstrate that widespread fatigue damage will not occur within the design service goal. Experimental study was focused on the crack growth in a model specimen the geometry of witch corresponds to Ayres Loadmaster LM200 wig spar. Fatigue crack initiated on sharp notches in a rivet hole. In the first period, the flange plane covers the web and thus no direct monitoring of the crack growth in web was possible. Macroscopic data was completed with fractographic results. Measurement of striation spacing allowed the reconstruction of growth of four fatigue cracks (two in the web and two in the flange plate). Precision of the fractographics reconstruction results strongly depends on the volume and the quality of input information.

Anglický abstrakt

One of the most important parts of the damage-tolerance evaluation of aircraft structure is full-scale fatigue test. This test must demonstrate that widespread fatigue damage will not occur within the design service goal. Experimental study was focused on the crack growth in a model specimen the geometry of witch corresponds to Ayres Loadmaster LM200 wig spar. Fatigue crack initiated on sharp notches in a rivet hole. In the first period, the flange plane covers the web and thus no direct monitoring of the crack growth in web was possible. Macroscopic data was completed with fractographic results. Measurement of striation spacing allowed the reconstruction of growth of four fatigue cracks (two in the web and two in the flange plate). Precision of the fractographics reconstruction results strongly depends on the volume and the quality of input information.

Klíčová slova v angličtině

fatigue life, residual static strangth, fractographic analysis

Autoři

AUGUSTIN, P.

Vydáno

12. 11. 2003

Nakladatel

Institute of Materials Research of Slovak Academy of Sciences

Místo

Košice

ISBN

80-968543-2-1

Kniha

Fractography 2003

Strany od

283

Strany do

290

Strany počet

8

BibTex

@inproceedings{BUT9187,
  author="Petr {Augustin}",
  title="Fraktografická rekonstrukce časového průběhu únavového porušování nosníku křídla letounu",
  booktitle="Fractography 2003",
  year="2003",
  pages="8",
  publisher="Institute of Materials Research of Slovak Academy of Sciences",
  address="Košice",
  isbn="80-968543-2-1"
}