Formation of Intermetallic Phases in Fe-Al Binary Cold Spray Thick Deposit

JAN, V. PÁLENÍKOVÁ, L. ČUPERA, J. ČÍŽEK, J.

Originální název

Formation of Intermetallic Phases in Fe-Al Binary Cold Spray Thick Deposit

Typ

článek ve sborníku ve WoS nebo Scopus

Jazyk

angličtina

Originální abstrakt

Deposits of 60/40 at% Fe/Al were produced by low-pressure cold spray technique using heated air (300C, 15 bar) as working gas.Samples of the deposited material were then annealed isothermally at temperatures from 250C to 750C for two hours in argon protective atmosphere. Gradual evolution of intermetallic phases by diffusion mechanism at temperatures from 550C was observed. The evolved phases included metastable and stable phases close to Al3Fe, FeAl, Al5Fe2 and Al2Fe. The samples general shape was preserved during the heating process due to a rapid formation of intermetallic skeleton (at temperatures exceeding aluminum melting temperature).

Klíčová slova

Cold spray, titanium, aluminum, intermetallics

Autoři

JAN, V.; PÁLENÍKOVÁ, L.; ČUPERA, J.; ČÍŽEK, J.

Rok RIV

2014

Vydáno

21. 5. 2014

Nakladatel

DVS Media GmbH

Místo

Barcelona, Španělsko

ISBN

978-3-87155-574-9

Kniha

International Thermal Spray Conference 2014 Proceedings

Strany od

908

Strany do

912

Strany počet

4

BibTex

@inproceedings{BUT108213,
  author="Vít {Jan} and Lucie {Dyčková} and Jan {Čupera} and Jan {Čížek}",
  title="Formation of Intermetallic Phases in Fe-Al Binary Cold Spray Thick Deposit",
  booktitle="International Thermal Spray Conference 2014 Proceedings",
  year="2014",
  pages="908--912",
  publisher="DVS Media GmbH",
  address="Barcelona, Španělsko",
  isbn="978-3-87155-574-9"
}