Detail publikace

Densification of fine-grained alumina ceramics doped by magnesia, yttria and zirconia evaluated by two different sintering models

MACA, K. POUCHLÝ, V. BODIŠOVÁ, K. ŠVANCÁREK, P. GALUSEK, D.

Originální název

Densification of fine-grained alumina ceramics doped by magnesia, yttria and zirconia evaluated by two different sintering models

Typ

článek v časopise ve Web of Science, Jimp

Jazyk

angličtina

Originální abstrakt

The influence of various dopants (500 ppm MgO and Y2O3;250 ppm ZrO2) on sintering of fine-grained alumina ceramics was evaluated by high-temperature dilatometry. The apparent activation energy of sintering was estimated with the help of Master Sintering Curve and a model proposedby Wang and Raj. The densification kinetics was controlled by at least two mechanisms operating at low (higher activation energy) and high (loweractivation energy) densities. Good agreement between the activation energies calculated with both models was observed for low as well as forhigh densities. The lowest value of activation energy exhibited undoped alumina; the addition of MgO resulted in slight increase of the activationenergy. Y2O3and ZrO2significantly inhibited the densification, which was reflected in the higher sintering activation energies. The low activationenergies in the final sintering step indicates the importance of proper choice of sintering temperature, namely in the two-step sintering process.

Klíčová slova

Sintering; Alumina; Activation energy

Autoři

MACA, K.; POUCHLÝ, V.; BODIŠOVÁ, K.; ŠVANCÁREK, P.; GALUSEK, D.

Rok RIV

2014

Vydáno

1. 12. 2014

ISSN

0955-2219

Periodikum

Journal of the European Ceramic Society

Ročník

34

Číslo

16

Stát

Spojené království Velké Británie a Severního Irska

Strany od

4363

Strany do

4372

Strany počet

10

BibTex

@article{BUT109753,
  author="Karel {Maca} and Václav {Pouchlý} and Katarina {Drdlíková} and Peter {Švancárek} and Dušan {Galusek}",
  title="Densification of fine-grained alumina ceramics doped by magnesia, yttria and zirconia evaluated by two different sintering models",
  journal="Journal of the European Ceramic Society",
  year="2014",
  volume="34",
  number="16",
  pages="4363--4372",
  doi="10.1016/j.jeurceramsoc.2014.06.030",
  issn="0955-2219"
}