THE INFLUENCE OF SUBSTRATE PREPARATION, ANODIZATION CONDITIONS AND POST ANODIZING TREATMENT ON AAO MICROSTRUCTURE

JINDROVÁ, E. JAN, V. ČUPERA, J.

Originální název

THE INFLUENCE OF SUBSTRATE PREPARATION, ANODIZATION CONDITIONS AND POST ANODIZING TREATMENT ON AAO MICROSTRUCTURE

Typ

článek ve sborníku ve WoS nebo Scopus

Jazyk

angličtina

Originální abstrakt

Series of anodization experiments was conducted on pure aluminium (99,95 Goodfellow) substrates with the aim to map the possibilities and evaluate available techniques. Oxalic acid electrolyte was used for anodization at different voltage levels ranging from 20 to 60V, while current was always measured continuously during the experiment. The influence of substrate surface treatment, time and grain size of the substrate was documented for as anodized oxide structures using FEG-SEM. Well aligned and evenly distributed pores of the diameters ranging 20- 35 nm were achieved. Extremely fine pores down to 10 nm were achieved using the step-down technique governed by current limitation. Further post-anodizing treatment was evaluated - pore widening by chemical and electrochemical etching, which resulted in pores 80nm wide.

Klíčová slova

Anodic alumina, AAO, anodization, electrodeposition, nanowires

Autoři

JINDROVÁ, E.; JAN, V.; ČUPERA, J.

Rok RIV

2014

Vydáno

21. 5. 2014

ISBN

978-80-87294-52-9

Kniha

Metal 2014

Strany od

953

Strany do

957

Strany počet

5

BibTex

@inproceedings{BUT112198,
  author="Eva {Šťastná} and Vít {Jan} and Jan {Čupera}",
  title="THE INFLUENCE OF SUBSTRATE PREPARATION, ANODIZATION CONDITIONS AND POST
ANODIZING TREATMENT ON AAO MICROSTRUCTURE",
  booktitle="Metal 2014",
  year="2014",
  pages="953--957",
  isbn="978-80-87294-52-9"
}