HYPO-EUTECTOID NITI ALLOY MANUFACTURED BY CGDS POWDER MIX DEPOSITION AND HEAT TREATEMENT

JAN, V. ČÍŽEK, J. DYČKA, M. ČUPERA, J.

Originální název

HYPO-EUTECTOID NITI ALLOY MANUFACTURED BY CGDS POWDER MIX DEPOSITION AND HEAT TREATEMENT

Typ

konferenční sborník (ne článek)

Jazyk

angličtina

Originální abstrakt

Bi-metallic Ni-Ti deposits were produced by low-pressure cold spray with air as working gas. The chemical composition of the 8 mm thick deposit was kept in hypoeutectoid concentration of 92/8 at% Ti/Ni. Samples were annealed in argon protective atmosphere at temperatures from 500°C to 1000°C for two hours. Apart from slow cooling, quenching directly from the homogenization at 1000°C was conducted on some samples and subsequent evolution of precipitated eutectoid was studied. Microstructural changes of material character during annealing were evaluated together with changes in the character of fracture behaviour and local micro hardness of the evolved phases. Microstructure and chemistry was evaluated using analytical electron microscopy. DSC study was involved in order to characterize the precipitation behaviour under eutectoid temperature. Gradual evolution of intermetallic phases by diffusion mechanism was observed. The samples general shape was preserved during the heating process although formation of Kirkendall porosity was evident. First occurrence of intermetallic phases was observed at 600°C. The evolved phases incurred by diffusion mechanism and included phases close to Ti2Ni, TiNi, and TiNi3.

Klíčová slova

Cold Spray, reaction synthesis, intermetallics, diffusion, metallic foam

Autoři

JAN, V.; ČÍŽEK, J.; DYČKA, M.; ČUPERA, J.

Vydáno

9. 12. 2015

Nakladatel

University of Limoges

Místo

Limoges

URL

http://www.unilim.fr/ript/

BibTex

@proceedings{BUT120151,
  editor="Vít {Jan} and Jan {Čížek} and Martin {Dyčka} and Jan {Čupera}",
  title="HYPO-EUTECTOID NITI ALLOY MANUFACTURED BY CGDS POWDER MIX DEPOSITION AND HEAT TREATEMENT",
  year="2015",
  publisher="University of Limoges",
  address="Limoges",
  url="http://www.unilim.fr/ript/"
}