Degradation analysis of GaAs solar cells at thermal stress

PAPEŽ, N. SOBOLA, D. ŠKARVADA, P. ŠKVARENINA, Ľ. HEMZAL, D. TOFEL, P. GRMELA, L.

Originální název

Degradation analysis of GaAs solar cells at thermal stress

Typ

abstrakt

Jazyk

angličtina

Originální abstrakt

The work focuses on the study of the stability of structure and electrical parameters of commercially available photovoltaic cells based on GaAs with Ge substrate. Solar cells of this type are used especially in adverse environments such as space applications, so their working parameters should be stable even under extreme operating conditions. Solar cells were irradiated by focused ion beam (FIB). Artificial defects with different size were created for study of dependence of characteristics on presence of micro and nano defects in structure. Afterwards original and defected solar cells by FIB were studied at different temperatures, ranging from room temperature up to 350 °C. Changes of electrical characteristics of the cells were recorded in the form of noise measurements for examination of distinctions in the pn-junction and in the form of current-voltage characteristics in light and dark for comparison of the cells performance. Infrared camera showed the thermal irradiation of the stressed and damaged part and support to localize the defected areas. Atomic force microscope (AFM) was applied for observation of changes in three-dimensional topography with high resolution. Scanning electron microscope (SEM) with energy-dispersive x-ray spectroscopy (EDX) showed morphology of the solar cells and provided the elemental analysis of the samples. Raman spectroscopy provided a structural fingerprint and helped to evaluate influence of induced degradation methods. Variation of morphology and composition were compared, detected and well-observed, furthermore electrical measurements proved the solar cells to be stable under temperature stresses.

Klíčová slova

AFM, SEM, FIB, EDX, Raman spectroscopy, noise, CV characteristics, GaAs, thermal annealing

Autoři

PAPEŽ, N.; SOBOLA, D.; ŠKARVADA, P.; ŠKVARENINA, Ľ.; HEMZAL, D.; TOFEL, P.; GRMELA, L.

Vydáno

20. 11. 2017

Nakladatel

Comenius University

Místo

Bratislava

ISBN

978-80-223-4411-1

Kniha

Progress in Applied Surface, Interface and Thin Film Science - Solar Renewable Energy News 2017

Strany od

105

Strany do

105

Strany počet

1

BibTex

@misc{BUT142561,
  author="Nikola {Papež} and Dinara {Sobola} and Pavel {Škarvada} and Ľubomír {Škvarenina} and Dušan {Hemzal} and Pavel {Tofel} and Lubomír {Grmela}",
  title="Degradation analysis of GaAs solar cells at thermal stress",
  booktitle="Progress in Applied Surface, Interface and Thin Film Science - Solar Renewable Energy News 2017",
  year="2017",
  pages="105--105",
  publisher="Comenius University",
  address="Bratislava",
  isbn="978-80-223-4411-1",
  note="abstract"
}