Analysis of Corrosion resistance of Heat Exchanger Plates Made of AISI 316L Steel

JULIŠ, M. KLAKURKOVÁ, L. GEJDOŠ, P.

Originální název

Analysis of Corrosion resistance of Heat Exchanger Plates Made of AISI 316L Steel

Typ

článek ve sborníku ve WoS nebo Scopus

Jazyk

angličtina

Originální abstrakt

For the corrosion resistance analysis of heat exchanger plates (made of AISI 316L steel) samples with visible damage were delivered. A major part of the surface damages was located at places of "close proximity" (or surface contact) of individual plates. Some of the samples submitted exhibited unequal layers of sediments, which indicated different flow velocities of the operating fluid through the plates. At some sedimentationfree sites in the upper part of the plates (high velocity flow), most of the surface damage was detected in the "near contact" areas as well as outside of them. On the other hand, in the area of the lower part of the plates, where the sediment deposition was massive (the lowest velocity flow), the least surface damage was observed. The results of the chemical composition analyses showed a lower amount of molybdenum and a higher amount of phosphorus for all samples. The contents of the key elements necessary for the corrosion resistance (chromium and nickel) were only just above the lower limit of the prescribed chemical composition interval. For a detailed study of surface damage, selected defects were observed and documented using scanning electron microscopy. Localized damage showed intercrystalline failure of material with a typical surface morphology degraded in consequence of cavitation damage under hydrodynamic stress.

Klíčová slova

AISI 316L steel; corrosion resistance; scanning electron microscopy; heat exchanger; metallography; fractography

Autoři

JULIŠ, M.; KLAKURKOVÁ, L.; GEJDOŠ, P.

Vydáno

16. 11. 2020

Nakladatel

Trans Tech Publications Ltd

Místo

Switzerland

ISSN

1662-9507

Periodikum

Defect and Diffusion Forum

Ročník

45

Stát

Švýcarská konfederace

Strany od

245

Strany do

250

Strany počet

6

URL

https://www.scientific.net/DDF.405.245

BibTex

@inproceedings{BUT159336,
  author="Martin {Juliš} and Lenka {Klakurková} and Pavel {Gejdoš}",
  title="Analysis of Corrosion resistance of Heat Exchanger Plates Made of AISI 316L Steel",
  booktitle="Metallography & Fractography 2019",
  year="2020",
  journal="Defect and Diffusion Forum",
  volume="45",
  pages="245--250",
  publisher="Trans Tech Publications Ltd",
  address="Switzerland",
  doi="10.4028/www.scientific.net/DDF.405.245",
  issn="1662-9507",
  url="https://www.scientific.net/DDF.405.245"
}