Corrosion Resistance of Ferritic Stainless Steel X12Cr13 After Application of Low-Temperature and High-Temperature Plasma Nitriding

KUSMIČ, D. ČECH, O. KLAKURKOVÁ, L.

Originální název

Corrosion Resistance of Ferritic Stainless Steel X12Cr13 After Application of Low-Temperature and High-Temperature Plasma Nitriding

Typ

článek v časopise ve Web of Science, Jimp

Jazyk

angličtina

Originální abstrakt

The impact of plasma nitriding process on corrosion resistance of ferrettic stainless steel (FSS) was evaluated in this study. The FSS X12Cr13 (AISI 410) was subjected to low-temperature plasma nitriding (LTPN) treatment at a temperature of 400°C in 3H2:1N2 (l/h) and in 1H2:3N2 (l/h) reverse working atmosphere (LTPN-R) and to high-temperature plasma nitriding (HTPN) treatment at 550 °C for 15 h. The microstructure and microhardness of the untreated and nitrided stainless steel were evaluated. The corrosion properties of the untreated and plasma nitrided steel samples were evaluated using the anodic potentiodynamic polarization tests in neutral 2.5% NaCl deaerated solution. The phase analysis showed that LTPN and LTPN-R treatment on the AISI 410 steel led to the formation of αN layer (nitrogen expanded ferrite) accompanied by Fe3C and Fe4N iron nitrides and CrN. The HTPN technique led additionally to the formation of an increased volume of Cr4N4 chromium nitrides and Cr15Fe7C6 chromium iron carbide. The plasma nitriding process significantly increased the microhardness of the ferritic stainless steel. The pitting was evaluated, and the pitting coefficient was calculated. The electrochemical corrosion tests showed the best corrosion resistance of the untreated X12Cr13 stainless steel, only slightly increased corrosion rates of LTPN and LTPN-R techniques, and extreme corrosion rates after application of the HTPN technique, causing Cr depletion and thereby suppressing the ability to passivation.

Klíčová slova

corrosion resistance; ferritic stainless steel; plasma nitriding

Autoři

KUSMIČ, D.; ČECH, O.; KLAKURKOVÁ, L.

Vydáno

10. 2. 2021

Nakladatel

Institute of Technology and Production Management University of J.E. Purkyne

Místo

Ústí nad Labem

ISSN

1213-2489

Periodikum

Manufacturing TECHNOLOGY

Ročník

21

Číslo

1

Stát

Česká republika

Strany od

98

Strany do

104

Strany počet

7

URL

BibTex

@article{BUT176119,
  author="David {Kusmič} and Ondřej {Čech} and Lenka {Klakurková}",
  title="Corrosion Resistance of Ferritic Stainless Steel X12Cr13 After Application of Low-Temperature and High-Temperature Plasma Nitriding",
  journal="Manufacturing TECHNOLOGY",
  year="2021",
  volume="21",
  number="1",
  pages="98--104",
  doi="10.21062/mft.2021.013",
  issn="1213-2489",
  url="https://doi.org/10.21062/mft.2021.013"
}