Detail publikace

Reoxidation phenomena in ferrous castings

ELBEL, T., ŠENBERGER, J., ZÁDĚRA, A.

Originální název

Reoxidation phenomena in ferrous castings

Typ

článek ve sborníku ve WoS nebo Scopus

Jazyk

angličtina

Originální abstrakt

Recent advances in understanding the metal-casting processes into green sand moulds have indicated that reoxidation plays a key role in the quality control of castings. As the liquid metal enters the mould cavity, thermal degradation of binders, water, and additives produces large quantities of gases and vapours. Air oxygen, mould atmosphere or oxides in the moulding sand can reoxidize the metal flow. Imperfect filling of castings induces agitation of the metal flow with oxygen present in gases and vapours, which results in secondary oxidation or the so-called metal reoxidation. Reoxidation processes in liquid metal can cause a number of defects in iron and steel castings.

Klíčová slova v angličtině

reoxidation, activity of oxygen, incoulation of melts

Autoři

ELBEL, T., ŠENBERGER, J., ZÁDĚRA, A.

Rok RIV

2005

Vydáno

14. 9. 2005

Nakladatel

Društvo Livarjev Slovenije

Místo

Ljubljana

Strany od

47

Strany do

56

Strany počet

10

BibTex

@inproceedings{BUT20429,
  author="Tomáš {Elbel} and Jaroslav {Šenberger} and Antonín {Záděra}",
  title="Reoxidation phenomena in ferrous castings",
  booktitle="Conference Proceedings International 45th Foundry Conference",
  year="2005",
  pages="10",
  publisher="Društvo Livarjev Slovenije",
  address="Ljubljana"
}