Nanostructure Characterization of IN738LC Superalloy Fatigued at High Temperature

PETRENEC, M. STRUNZ, P. GASSER, U. HECZKO, M. ZÁLEŠÁK, J. POLÁK, J.

Originální název

Nanostructure Characterization of IN738LC Superalloy Fatigued at High Temperature

Typ

článek ve sborníku ve WoS nebo Scopus

Jazyk

angličtina

Originální abstrakt

The nanostructure of Inconel 738LC Ni-superalloy strengthened by trimodal gamma precipitates distribution was investigated after Low Cycle Fatigue (LCF) loading at temperature 700C. Different microscopic techniques as Scanning Electron Microscope (SEM) equipped with STEM detector, transmission Kikuchi diffraction in the SEM, transmission electron microscope (TEM) in the bright field mode and high resolution transmission electron microscopes (HRTEM) in STEM mode were used for the characterization and quantification of superalloy nanostructure. The characteristic morphology of gamma precipitates was examined by ex-situ and in-situ Small Angle Neutron Scattering (SANS) at high temperatures. All adopted microscopic techniques indicate that the morphology of gamma precipitates distributed in the gamma matrix as received state corresponds to two types, i.e. large cuboid-like precipitates with the size around 670 nm, and the spherical precipitates with the diameter 52 nm. After the LCF tests at temperature 700C, the ex-situ SANS measurement yielded additional scattering intensities coming from another small gamma precipitates with estimated size up to 10 nm. Thin foils were observed in SEM equipped with STEM detector, in TEM and HRTEM. These observations documented the size 7 nm and evolution of distribution of these precipitates. It was concluded from in-situ SANS experiments that the smallest gamma precipitates arise regardless the application of the mechanical load. These very small precipitates have profound effect on the LCF resistance of the alloy at 700C since dislocations are effectively pinned by these small gamma precipitates as was directly observed by STEM detector in SEM and using TEM in STEM mode.

Klíčová slova

superalloys, nano-precipitation, neutron scattering, STEM detector, TEM

Autoři

PETRENEC, M.; STRUNZ, P.; GASSER, U.; HECZKO, M.; ZÁLEŠÁK, J.; POLÁK, J.

Rok RIV

2013

Vydáno

16. 10. 2013

Nakladatel

Tanger, Ltd.

Místo

Czech Republic

ISBN

978-80-87294-44-4

Kniha

NANOCON 2013 Conference Proceedings

Edice

1st Edition, 2014

Číslo edice

1

ISSN

NEUVEDENO

Strany od

712

Strany do

717

Strany počet

7

BibTex

@inproceedings{BUT108925,
  author="PETRENEC, M. and STRUNZ, P. and GASSER, U. and HECZKO, M. and ZÁLEŠÁK, J. and POLÁK, J.",
  title="Nanostructure Characterization of IN738LC Superalloy Fatigued at High Temperature",
  booktitle="NANOCON 2013 Conference Proceedings",
  year="2013",
  series="1st Edition, 2014",
  number="1",
  pages="712--717",
  publisher="Tanger, Ltd.",
  address="Czech Republic",
  isbn="978-80-87294-44-4"
}