Electrospinning and thermal treatment of yttria doped zirconia fibres

ČÁSTKOVÁ, K. MACA, K. SEKANINOVÁ, J. NEMČOVSKÝ, J. CIHLÁŘ, J.

Originální název

Electrospinning and thermal treatment of yttria doped zirconia fibres

Typ

článek v časopise ve Web of Science, Jimp

Jazyk

angličtina

Originální abstrakt

As compared to a bulk material, the fibres exhibit novel physical and chemical properties arising from their unique geometric features such as high surface area, surface to volume ratio and small fibre diameter. This paper is focused on the fabrication of nanosized 8 mol% yttria doped zirconia fibres by electrospinning from propoxide/polyvinylpyrrolidonebased precursors and physical-chemical characterization of the ceramic fibres with an energy application potential. Fully crystalline composition of cubic zirconia was detected after fibre heat treatment at 700 °C. The fibre morphology was changed with increasing temperature from flexible nonsintered nanoparticle system at 700 °C through porous nanograin structure at 900 °C and nonporous structure with coarser nanograins at 1100 °C to fragile chain-like fibre structure formed of elongated submicrometer grains at 1300–1450 °C. The densification and grain growth kinetics were described in two stages in the temperature range from 700 °C up to 1450 °C.

Klíčová slova

Nanofibre Zirconia Electrospinning Sintering

Autoři

ČÁSTKOVÁ, K.; MACA, K.; SEKANINOVÁ, J.; NEMČOVSKÝ, J.; CIHLÁŘ, J.

Vydáno

1. 7. 2017

ISSN

0272-8842

Periodikum

Ceramics International

Ročník

43

Číslo

10

Stát

Spojené království Velké Británie a Severního Irska

Strany od

7581

Strany do

7587

Strany počet

7

BibTex

@article{BUT135124,
  author="Klára {Částková} and Karel {Maca} and Jana {Ručková} and Jakub {Nemčovský} and Jaroslav {Cihlář}",
  title="Electrospinning and thermal treatment of yttria doped zirconia fibres",
  journal="Ceramics International",
  year="2017",
  volume="43",
  number="10",
  pages="7581--7587",
  doi="10.1016/j.ceramint.2017.03.050",
  issn="0272-8842"
}