Shrinkage, weight loss and fracture parameters of selected polymer-modified cement mortars during ageing

KUCHARCZYKOVÁ, B. ŠIMONOVÁ, H. KERŠNER, Z. KOCÁB, D.

Originální název

Shrinkage, weight loss and fracture parameters of selected polymer-modified cement mortars during ageing

Typ

článek v časopise - ostatní, Jost

Jazyk

angličtina

Originální abstrakt

Results of pilot experiments focused on monitoring of shrinkage, weight loss and mechanical fracture properties of two selected polymer-modified cement mortars (PCM) during their aging are presented in the paper. Comparison of the measurement results was carried out on the test specimens at the age of 3, 28, and 90 days. The results show that even the specimens made from PCMs, for which the manufacturer declares no shrinkage, shrank considerably. The results also show that the development of mechanical fracture parameters during ageing of these materials differs from generally expected trends and thus the monitoring of these parameters is recommended.

Klíčová slova

Polymer-modified cement mortar, shrinkage, weight loss, modulus of elasticity, fracture toughness, fracture energy

Autoři

KUCHARCZYKOVÁ, B.; ŠIMONOVÁ, H.; KERŠNER, Z.; KOCÁB, D.

Vydáno

1. 6. 2017

Nakladatel

VŠB – Technical University of Ostrava

Místo

Ostrava

ISSN

1213-1962

Periodikum

Sborník vědeckých prací Vysoké školy báňské – Technické univerzity Ostrava

Ročník

17

Číslo

1

Stát

Česká republika

Strany od

122

Strany do

130

Strany počet

9

URL

http://www.degruyter.com/view/j/tvsb.2017.17.issue-1/tvsb-2017-0014/tvsb-2017-0014.xml?format=INT

Plný text v Digitální knihovně

http://hdl.handle.net/11012/69320

BibTex

@article{BUT137684,
  author="Barbara {Kucharczyková} and Hana {Šimonová} and Zbyněk {Keršner} and Dalibor {Kocáb}",
  title="Shrinkage, weight loss and fracture parameters of selected polymer-modified cement mortars during ageing",
  journal="Sborník vědeckých prací Vysoké školy báňské – Technické univerzity Ostrava",
  year="2017",
  volume="17",
  number="1",
  pages="122--130",
  doi="10.1515/tvsb-2017-0014",
  issn="1213-1962",
  url="http://www.degruyter.com/view/j/tvsb.2017.17.issue-1/tvsb-2017-0014/tvsb-2017-0014.xml?format=INT"
}