Originální abstrakt

Polycaprolactone is known as biocompatible material for long time and it is considered as possible material for bioscaffolds. Since natural structure of hard tissues (bones) and most of soft tissues (skin, neural tissue) is fibrous, there are attempts to mimic such a structure. Polycaprolactone (PCL) nanofibers with diameter of approximately 180 nm were prepared by electrospinning method. For better biocompatibility and bioactivity, a composite fibrous structure was prepared. Hydroxyapatite nanoparticles were synthetized via precipitation reaction and further hydrothermal treatment. The ceramic particles were added to modified polycaprolactone precursor and the solution was electrospun. The prepared fibers and as well as dried original precursor were in-vitro tested for cytotoxicity by direct contact test. Mouse fibroblast from L929 line were used for cell cultivation. It was found out that fibrous structure and presence of ceramic particles have a positive influence on cell activity and proliferation – the growth rate of the cells was significantly higher compared to bulk polymer precursor.

Klíčová slova

Nanofibers, electrospinning, biocompatibility, polycaprolactone

Autoři

ŠŤASTNÁ, E.; ČÁSTKOVÁ, K.

Vydáno

1. 1. 2019

ISBN

978-80-87294-89-5

Kniha

10TH ANNIVERSARY INTERNATIONAL CONFERENCE ON NANOMATERIALS - RESEARCH & APPLICATION (NANOCON 2018 (R))

Strany od

472

Strany do

476

Strany počet

5

BibTex

@inproceedings{BUT153362,
  author="Eva {Šťastná} and Klára {Částková}",
  title="Electrospinning and biocompatibility of polymer-ceramic nanofibers for tissue engineering",
  booktitle="10TH ANNIVERSARY INTERNATIONAL CONFERENCE ON NANOMATERIALS - RESEARCH & APPLICATION (NANOCON 2018 (R))",
  year="2019",
  pages="472--476",
  isbn="978-80-87294-89-5"
}